i-XCITE LC N

i-XCITE LC N is a light-cured, nano-hybrid composite meticulously designed for both direct and indirect restorative procedures.
Engineered for optimal performance, its bioinert, radiopaque formulation ensures high strength, excellent abrasion resistance, and long-term durability
With shades matching the VITA® shade guide, this composite is offering natural aesthetics and superior color stability, making it ideal for anterior and posterior restorations.

Clinical Indications

For direct restorations of class I, II, III, IV and V cavities
For indirect restorations such as inlays, onlays
For Core Build Ups

Key Features

High inorganic filler load increase mechanical strength to withstand mastication forces
Extremely homogeneous and smooth consistency ensures precise handling and effortless sculptability
Highly resistant to wear, providing reliable long-term performance
Radiopaque for accurate radiographic evaluation
Biocompatible composition ensures safety in clinical use
Achieves a lasting high-gloss finish through fast and easy polishing
Combines superior aesthetics with durable, long-lasting shades for natural-looking results

Physical Properties

Silica/barium glass filler: main glass cluster size 0.25-3.0 µm
Inorganic filer loading by weight 77,92%
Based on: UDMA EBPADMA Bis-GMA, TEGDMA
Flexural strength: 119.2 ± 6.6 MPa
Water sorption: 17.99 ± 0.32 μg/mm³
Water solubility: 0.68 ± 0.24 μg/mm³
Light curing time: 20 seconds
Depth of cure: 2.50 ± 0.03 mm